Filament extrusion always stops at some point during print

The name of the pictureThe name of the pictureThe name of the pictureClash Royale CLAN TAG#URR8PPP












3












$begingroup$


I own a Creality CR-10 (using Ultimaker Cura for slicing) and I am experiencing terrible printing problems.



My problem: I am not able to print anything that takes several hours to print. For parts printed in 30 minutes or so, my printer usually works.



The prints end up like this (unfinished and with a lot of stringing)



fail



This below is actually the best result I got so far.. (important note: there is no under extrusion during the print, it suddenly stops out of nowhere..)
fail2
(Although I have to use terrible retraction settings and need a lot of post processing because of all the stringing - you might have an answer for that too.. I just couldnt get the 3d printer to print parts properly with good retraction settings.)



The problem is that at some point of the print, no more (PLA) material is extruded and the printer moves without actually printing anything. The first couple of layers usually work (you can see that in the images) but after wasting almost 600 grams of PLA, I am not able to find a solution myself.



.



I have some suspicions:



Could the problem be the angle, the PLA is inserted into the feeder? (so that it is almost a 90 degree bend)? The filament comes from a spool in the right hand side. But I dont think that this would cause such a problem..



Angle of inserted filament



Is it a software problem? Here are all my cura settings (I even reduced the printing speed to 30mm/s at 205°C - still didnt work..) :-(



enter image description hereenter image description hereenter image description here



Could the length of the bowden tube and it tangling up be a problem? (as you can see in the image below)
enter image description here



And annother important thing: The feeder always grinds into the filament (even at those low retraction settings) and it is always very hard to pull the filament out of the bowden after a failed print. Sometimes its almost impossible and i have to use heavy tools for it.. that should be the probelem
enter image description here



I already did some atomic pulls, replaced the nozzle and switched the bowden tube.



I have a dream: My printer printing a part without any stringing and actually finishing the print. Please help me to achieve this dream..



Thank you for your help in advance. :)



(and the filament I used, sorry for the bad quality of the pic)
enter image description here










share|improve this question











$endgroup$
















    3












    $begingroup$


    I own a Creality CR-10 (using Ultimaker Cura for slicing) and I am experiencing terrible printing problems.



    My problem: I am not able to print anything that takes several hours to print. For parts printed in 30 minutes or so, my printer usually works.



    The prints end up like this (unfinished and with a lot of stringing)



    fail



    This below is actually the best result I got so far.. (important note: there is no under extrusion during the print, it suddenly stops out of nowhere..)
    fail2
    (Although I have to use terrible retraction settings and need a lot of post processing because of all the stringing - you might have an answer for that too.. I just couldnt get the 3d printer to print parts properly with good retraction settings.)



    The problem is that at some point of the print, no more (PLA) material is extruded and the printer moves without actually printing anything. The first couple of layers usually work (you can see that in the images) but after wasting almost 600 grams of PLA, I am not able to find a solution myself.



    .



    I have some suspicions:



    Could the problem be the angle, the PLA is inserted into the feeder? (so that it is almost a 90 degree bend)? The filament comes from a spool in the right hand side. But I dont think that this would cause such a problem..



    Angle of inserted filament



    Is it a software problem? Here are all my cura settings (I even reduced the printing speed to 30mm/s at 205°C - still didnt work..) :-(



    enter image description hereenter image description hereenter image description here



    Could the length of the bowden tube and it tangling up be a problem? (as you can see in the image below)
    enter image description here



    And annother important thing: The feeder always grinds into the filament (even at those low retraction settings) and it is always very hard to pull the filament out of the bowden after a failed print. Sometimes its almost impossible and i have to use heavy tools for it.. that should be the probelem
    enter image description here



    I already did some atomic pulls, replaced the nozzle and switched the bowden tube.



    I have a dream: My printer printing a part without any stringing and actually finishing the print. Please help me to achieve this dream..



    Thank you for your help in advance. :)



    (and the filament I used, sorry for the bad quality of the pic)
    enter image description here










    share|improve this question











    $endgroup$














      3












      3








      3





      $begingroup$


      I own a Creality CR-10 (using Ultimaker Cura for slicing) and I am experiencing terrible printing problems.



      My problem: I am not able to print anything that takes several hours to print. For parts printed in 30 minutes or so, my printer usually works.



      The prints end up like this (unfinished and with a lot of stringing)



      fail



      This below is actually the best result I got so far.. (important note: there is no under extrusion during the print, it suddenly stops out of nowhere..)
      fail2
      (Although I have to use terrible retraction settings and need a lot of post processing because of all the stringing - you might have an answer for that too.. I just couldnt get the 3d printer to print parts properly with good retraction settings.)



      The problem is that at some point of the print, no more (PLA) material is extruded and the printer moves without actually printing anything. The first couple of layers usually work (you can see that in the images) but after wasting almost 600 grams of PLA, I am not able to find a solution myself.



      .



      I have some suspicions:



      Could the problem be the angle, the PLA is inserted into the feeder? (so that it is almost a 90 degree bend)? The filament comes from a spool in the right hand side. But I dont think that this would cause such a problem..



      Angle of inserted filament



      Is it a software problem? Here are all my cura settings (I even reduced the printing speed to 30mm/s at 205°C - still didnt work..) :-(



      enter image description hereenter image description hereenter image description here



      Could the length of the bowden tube and it tangling up be a problem? (as you can see in the image below)
      enter image description here



      And annother important thing: The feeder always grinds into the filament (even at those low retraction settings) and it is always very hard to pull the filament out of the bowden after a failed print. Sometimes its almost impossible and i have to use heavy tools for it.. that should be the probelem
      enter image description here



      I already did some atomic pulls, replaced the nozzle and switched the bowden tube.



      I have a dream: My printer printing a part without any stringing and actually finishing the print. Please help me to achieve this dream..



      Thank you for your help in advance. :)



      (and the filament I used, sorry for the bad quality of the pic)
      enter image description here










      share|improve this question











      $endgroup$




      I own a Creality CR-10 (using Ultimaker Cura for slicing) and I am experiencing terrible printing problems.



      My problem: I am not able to print anything that takes several hours to print. For parts printed in 30 minutes or so, my printer usually works.



      The prints end up like this (unfinished and with a lot of stringing)



      fail



      This below is actually the best result I got so far.. (important note: there is no under extrusion during the print, it suddenly stops out of nowhere..)
      fail2
      (Although I have to use terrible retraction settings and need a lot of post processing because of all the stringing - you might have an answer for that too.. I just couldnt get the 3d printer to print parts properly with good retraction settings.)



      The problem is that at some point of the print, no more (PLA) material is extruded and the printer moves without actually printing anything. The first couple of layers usually work (you can see that in the images) but after wasting almost 600 grams of PLA, I am not able to find a solution myself.



      .



      I have some suspicions:



      Could the problem be the angle, the PLA is inserted into the feeder? (so that it is almost a 90 degree bend)? The filament comes from a spool in the right hand side. But I dont think that this would cause such a problem..



      Angle of inserted filament



      Is it a software problem? Here are all my cura settings (I even reduced the printing speed to 30mm/s at 205°C - still didnt work..) :-(



      enter image description hereenter image description hereenter image description here



      Could the length of the bowden tube and it tangling up be a problem? (as you can see in the image below)
      enter image description here



      And annother important thing: The feeder always grinds into the filament (even at those low retraction settings) and it is always very hard to pull the filament out of the bowden after a failed print. Sometimes its almost impossible and i have to use heavy tools for it.. that should be the probelem
      enter image description here



      I already did some atomic pulls, replaced the nozzle and switched the bowden tube.



      I have a dream: My printer printing a part without any stringing and actually finishing the print. Please help me to achieve this dream..



      Thank you for your help in advance. :)



      (and the filament I used, sorry for the bad quality of the pic)
      enter image description here







      print-quality filament pla cr-10






      share|improve this question















      share|improve this question













      share|improve this question




      share|improve this question








      edited Jan 16 at 14:12









      0scar

      11.1k31546




      11.1k31546










      asked Jan 16 at 13:39









      DonaldEnteDonaldEnte

      1226




      1226




















          3 Answers
          3






          active

          oldest

          votes


















          2












          $begingroup$

          I've had a similar issue once. It was caused by very slight misconfiguration in filament feed rate (my printer tried to push through too much filament). While it was technically overextruding, I didn't realize that until I measured my extrusion lengths. Overextrusion could also contribute to stringing.



          When you pull out the filament from your extruder after a print failure, does it have a thicker end? If so, it could be a sign of trying to push too much filament.



          On the left is the filament I pulled from the extruder after a normal print - you can see it only gets thinner and has a long end. In the middle is a very pathological case - that shouldn't happen unless something is very wrong. On the right is how the filament was when I had my extruder feed rate misconfigured - you can see the dents from gear biting too hard into it, and a slight bulge.
          different filament ends



          What I think happened in my case, is that filament gets melted in the hotend, some of it gets pushed through the nozzle, the excess wells up into the heatbreak, where it solidifies and bonds to walls, causing blockage and difficulties pulling it out.



          As to how to fix it (if it's indeed the cause) - if you configured printer's firmware yourself, you may need to tweak steps/mm for the extruder.
          It looks like your printer runs Marlin firmware, which allows you to configure steps/mm from your LCD. You could also use PC software such as Pronterface to connect to your printer and tweak steps/mm parameters (alongside with other things). Here's a guide for checking and adjusting extruder steps/mm value. Though thick marker lines are not the best for measurement.

          You can also measure how much filament exits your bowden tube with calipers when you move it from printer LCD.

          If you don't want to mess around with firmware and steps/mm settings, you can adjust flow rate in Cura, although in that case you'll have to experiment with it and waste even more filament. I'd advise you to check for other possible issues first.



          As the other answer has said, this could be caused by temperature creep too, with similar symptoms - filament melting in the heatbreak.



          A long and bendy bowden tube could cause issues, but I'd expect underextrusion+grinding from that, whereas you don't see any underextrusion. Just to be sure, you could try pushing filament by hand (with other hand holding the lever on your extruder to release the filament) - it shouldn't take much force to move it all the way to extruder, and it shouldn't take much force to push it through the hotend either.

          Yet another thing to check is whether your filament gets dented by the extruder gear during normal print. Just insert it until the hotend without holding the lever on extruder and pull it out - it should be as smooth and round as it was before insertion. If it has dents from the extruder gear, that could also be the source of your problems. In that case, you'll need to reduce tension on your extruder spring, or if it's non-adjustable, then get another spring or shorten the existing one.



          As the last thing to check, does this happen with other filaments, especially single-color ones? Maybe this particular filament doesn't play nice with your hotend because of those black dot inclusions.



          So, short list of things to check:



          1. Check extruder steps/mm


          2. Check force on pushing filament through bowden tube (by hand)


          3. Check extruder gear tension


          4. Try another filament






          share|improve this answer









          $endgroup$












          • $begingroup$
            Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
            $endgroup$
            – DonaldEnte
            Jan 17 at 19:59











          • $begingroup$
            One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
            $endgroup$
            – DonaldEnte
            Jan 17 at 20:13










          • $begingroup$
            @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
            $endgroup$
            – knah
            Jan 18 at 0:22










          • $begingroup$
            @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
            $endgroup$
            – 0scar
            Jan 18 at 10:26










          • $begingroup$
            Why did you add the middle piece of filament, it would never come out a tube like that...
            $endgroup$
            – 0scar
            Jan 18 at 10:30


















          6












          $begingroup$

          Stringing?



          The stringing is explained by your relatively low retraction settings, 1.5 mm is not much for a Bowden setup. As do too high printing temperatures.



          Stopping mid printing?



          What you are experiencing is called clogging, the extruder cannot push the filament through the hotend and cause the grinding you report. Clogging mid printing is usually caused by insufficient cooling (for the temperature you print at) of the cold end (causing heat creep; slowly increasing temperature of the heat break), especially all-metal hotend assemblies are notoriously known for this problem.



          Your Bowden tube does make a lot of kinks, maybe you can improve the path of the Bowden tube. Also if you are concerned about the sharp filament intake angle, you could print a filament guide:



          Creality CR-10 extruder assembly with filament guide






          share|improve this answer











          $endgroup$












          • $begingroup$
            Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
            $endgroup$
            – DonaldEnte
            Jan 16 at 14:40






          • 3




            $begingroup$
            @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
            $endgroup$
            – Pᴀᴜʟsᴛᴇʀ2
            Jan 16 at 14:45






          • 1




            $begingroup$
            Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
            $endgroup$
            – anaximander
            Jan 16 at 16:06



















          -1












          $begingroup$

          I had the same thing! On my anycubic I3 mega.



          Tried a lot of stuff and got so sick of it so I installed a 10:1 gearbox on my extruder motor. So now it provides 10x more torque and since I havent got the issue anymore where the extruder is just grinding on the filament and the motor is just skipping steps.



          No because of this and because my anycubic won't connect to a pc I can't change settings on my printer so I resolve the ratio with 1000% flow in my cura settings. And other stuff is also affected.



          But at least it won't stop and just be sitting there and skipping steps.






          share|improve this answer









          $endgroup$








          • 2




            $begingroup$
            This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
            $endgroup$
            – Davo
            Jan 18 at 13:04









          protected by 0scar Jan 18 at 9:04



          Thank you for your interest in this question.
          Because it has attracted low-quality or spam answers that had to be removed, posting an answer now requires 10 reputation on this site (the association bonus does not count).



          Would you like to answer one of these unanswered questions instead?














          3 Answers
          3






          active

          oldest

          votes








          3 Answers
          3






          active

          oldest

          votes









          active

          oldest

          votes






          active

          oldest

          votes









          2












          $begingroup$

          I've had a similar issue once. It was caused by very slight misconfiguration in filament feed rate (my printer tried to push through too much filament). While it was technically overextruding, I didn't realize that until I measured my extrusion lengths. Overextrusion could also contribute to stringing.



          When you pull out the filament from your extruder after a print failure, does it have a thicker end? If so, it could be a sign of trying to push too much filament.



          On the left is the filament I pulled from the extruder after a normal print - you can see it only gets thinner and has a long end. In the middle is a very pathological case - that shouldn't happen unless something is very wrong. On the right is how the filament was when I had my extruder feed rate misconfigured - you can see the dents from gear biting too hard into it, and a slight bulge.
          different filament ends



          What I think happened in my case, is that filament gets melted in the hotend, some of it gets pushed through the nozzle, the excess wells up into the heatbreak, where it solidifies and bonds to walls, causing blockage and difficulties pulling it out.



          As to how to fix it (if it's indeed the cause) - if you configured printer's firmware yourself, you may need to tweak steps/mm for the extruder.
          It looks like your printer runs Marlin firmware, which allows you to configure steps/mm from your LCD. You could also use PC software such as Pronterface to connect to your printer and tweak steps/mm parameters (alongside with other things). Here's a guide for checking and adjusting extruder steps/mm value. Though thick marker lines are not the best for measurement.

          You can also measure how much filament exits your bowden tube with calipers when you move it from printer LCD.

          If you don't want to mess around with firmware and steps/mm settings, you can adjust flow rate in Cura, although in that case you'll have to experiment with it and waste even more filament. I'd advise you to check for other possible issues first.



          As the other answer has said, this could be caused by temperature creep too, with similar symptoms - filament melting in the heatbreak.



          A long and bendy bowden tube could cause issues, but I'd expect underextrusion+grinding from that, whereas you don't see any underextrusion. Just to be sure, you could try pushing filament by hand (with other hand holding the lever on your extruder to release the filament) - it shouldn't take much force to move it all the way to extruder, and it shouldn't take much force to push it through the hotend either.

          Yet another thing to check is whether your filament gets dented by the extruder gear during normal print. Just insert it until the hotend without holding the lever on extruder and pull it out - it should be as smooth and round as it was before insertion. If it has dents from the extruder gear, that could also be the source of your problems. In that case, you'll need to reduce tension on your extruder spring, or if it's non-adjustable, then get another spring or shorten the existing one.



          As the last thing to check, does this happen with other filaments, especially single-color ones? Maybe this particular filament doesn't play nice with your hotend because of those black dot inclusions.



          So, short list of things to check:



          1. Check extruder steps/mm


          2. Check force on pushing filament through bowden tube (by hand)


          3. Check extruder gear tension


          4. Try another filament






          share|improve this answer









          $endgroup$












          • $begingroup$
            Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
            $endgroup$
            – DonaldEnte
            Jan 17 at 19:59











          • $begingroup$
            One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
            $endgroup$
            – DonaldEnte
            Jan 17 at 20:13










          • $begingroup$
            @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
            $endgroup$
            – knah
            Jan 18 at 0:22










          • $begingroup$
            @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
            $endgroup$
            – 0scar
            Jan 18 at 10:26










          • $begingroup$
            Why did you add the middle piece of filament, it would never come out a tube like that...
            $endgroup$
            – 0scar
            Jan 18 at 10:30















          2












          $begingroup$

          I've had a similar issue once. It was caused by very slight misconfiguration in filament feed rate (my printer tried to push through too much filament). While it was technically overextruding, I didn't realize that until I measured my extrusion lengths. Overextrusion could also contribute to stringing.



          When you pull out the filament from your extruder after a print failure, does it have a thicker end? If so, it could be a sign of trying to push too much filament.



          On the left is the filament I pulled from the extruder after a normal print - you can see it only gets thinner and has a long end. In the middle is a very pathological case - that shouldn't happen unless something is very wrong. On the right is how the filament was when I had my extruder feed rate misconfigured - you can see the dents from gear biting too hard into it, and a slight bulge.
          different filament ends



          What I think happened in my case, is that filament gets melted in the hotend, some of it gets pushed through the nozzle, the excess wells up into the heatbreak, where it solidifies and bonds to walls, causing blockage and difficulties pulling it out.



          As to how to fix it (if it's indeed the cause) - if you configured printer's firmware yourself, you may need to tweak steps/mm for the extruder.
          It looks like your printer runs Marlin firmware, which allows you to configure steps/mm from your LCD. You could also use PC software such as Pronterface to connect to your printer and tweak steps/mm parameters (alongside with other things). Here's a guide for checking and adjusting extruder steps/mm value. Though thick marker lines are not the best for measurement.

          You can also measure how much filament exits your bowden tube with calipers when you move it from printer LCD.

          If you don't want to mess around with firmware and steps/mm settings, you can adjust flow rate in Cura, although in that case you'll have to experiment with it and waste even more filament. I'd advise you to check for other possible issues first.



          As the other answer has said, this could be caused by temperature creep too, with similar symptoms - filament melting in the heatbreak.



          A long and bendy bowden tube could cause issues, but I'd expect underextrusion+grinding from that, whereas you don't see any underextrusion. Just to be sure, you could try pushing filament by hand (with other hand holding the lever on your extruder to release the filament) - it shouldn't take much force to move it all the way to extruder, and it shouldn't take much force to push it through the hotend either.

          Yet another thing to check is whether your filament gets dented by the extruder gear during normal print. Just insert it until the hotend without holding the lever on extruder and pull it out - it should be as smooth and round as it was before insertion. If it has dents from the extruder gear, that could also be the source of your problems. In that case, you'll need to reduce tension on your extruder spring, or if it's non-adjustable, then get another spring or shorten the existing one.



          As the last thing to check, does this happen with other filaments, especially single-color ones? Maybe this particular filament doesn't play nice with your hotend because of those black dot inclusions.



          So, short list of things to check:



          1. Check extruder steps/mm


          2. Check force on pushing filament through bowden tube (by hand)


          3. Check extruder gear tension


          4. Try another filament






          share|improve this answer









          $endgroup$












          • $begingroup$
            Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
            $endgroup$
            – DonaldEnte
            Jan 17 at 19:59











          • $begingroup$
            One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
            $endgroup$
            – DonaldEnte
            Jan 17 at 20:13










          • $begingroup$
            @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
            $endgroup$
            – knah
            Jan 18 at 0:22










          • $begingroup$
            @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
            $endgroup$
            – 0scar
            Jan 18 at 10:26










          • $begingroup$
            Why did you add the middle piece of filament, it would never come out a tube like that...
            $endgroup$
            – 0scar
            Jan 18 at 10:30













          2












          2








          2





          $begingroup$

          I've had a similar issue once. It was caused by very slight misconfiguration in filament feed rate (my printer tried to push through too much filament). While it was technically overextruding, I didn't realize that until I measured my extrusion lengths. Overextrusion could also contribute to stringing.



          When you pull out the filament from your extruder after a print failure, does it have a thicker end? If so, it could be a sign of trying to push too much filament.



          On the left is the filament I pulled from the extruder after a normal print - you can see it only gets thinner and has a long end. In the middle is a very pathological case - that shouldn't happen unless something is very wrong. On the right is how the filament was when I had my extruder feed rate misconfigured - you can see the dents from gear biting too hard into it, and a slight bulge.
          different filament ends



          What I think happened in my case, is that filament gets melted in the hotend, some of it gets pushed through the nozzle, the excess wells up into the heatbreak, where it solidifies and bonds to walls, causing blockage and difficulties pulling it out.



          As to how to fix it (if it's indeed the cause) - if you configured printer's firmware yourself, you may need to tweak steps/mm for the extruder.
          It looks like your printer runs Marlin firmware, which allows you to configure steps/mm from your LCD. You could also use PC software such as Pronterface to connect to your printer and tweak steps/mm parameters (alongside with other things). Here's a guide for checking and adjusting extruder steps/mm value. Though thick marker lines are not the best for measurement.

          You can also measure how much filament exits your bowden tube with calipers when you move it from printer LCD.

          If you don't want to mess around with firmware and steps/mm settings, you can adjust flow rate in Cura, although in that case you'll have to experiment with it and waste even more filament. I'd advise you to check for other possible issues first.



          As the other answer has said, this could be caused by temperature creep too, with similar symptoms - filament melting in the heatbreak.



          A long and bendy bowden tube could cause issues, but I'd expect underextrusion+grinding from that, whereas you don't see any underextrusion. Just to be sure, you could try pushing filament by hand (with other hand holding the lever on your extruder to release the filament) - it shouldn't take much force to move it all the way to extruder, and it shouldn't take much force to push it through the hotend either.

          Yet another thing to check is whether your filament gets dented by the extruder gear during normal print. Just insert it until the hotend without holding the lever on extruder and pull it out - it should be as smooth and round as it was before insertion. If it has dents from the extruder gear, that could also be the source of your problems. In that case, you'll need to reduce tension on your extruder spring, or if it's non-adjustable, then get another spring or shorten the existing one.



          As the last thing to check, does this happen with other filaments, especially single-color ones? Maybe this particular filament doesn't play nice with your hotend because of those black dot inclusions.



          So, short list of things to check:



          1. Check extruder steps/mm


          2. Check force on pushing filament through bowden tube (by hand)


          3. Check extruder gear tension


          4. Try another filament






          share|improve this answer









          $endgroup$



          I've had a similar issue once. It was caused by very slight misconfiguration in filament feed rate (my printer tried to push through too much filament). While it was technically overextruding, I didn't realize that until I measured my extrusion lengths. Overextrusion could also contribute to stringing.



          When you pull out the filament from your extruder after a print failure, does it have a thicker end? If so, it could be a sign of trying to push too much filament.



          On the left is the filament I pulled from the extruder after a normal print - you can see it only gets thinner and has a long end. In the middle is a very pathological case - that shouldn't happen unless something is very wrong. On the right is how the filament was when I had my extruder feed rate misconfigured - you can see the dents from gear biting too hard into it, and a slight bulge.
          different filament ends



          What I think happened in my case, is that filament gets melted in the hotend, some of it gets pushed through the nozzle, the excess wells up into the heatbreak, where it solidifies and bonds to walls, causing blockage and difficulties pulling it out.



          As to how to fix it (if it's indeed the cause) - if you configured printer's firmware yourself, you may need to tweak steps/mm for the extruder.
          It looks like your printer runs Marlin firmware, which allows you to configure steps/mm from your LCD. You could also use PC software such as Pronterface to connect to your printer and tweak steps/mm parameters (alongside with other things). Here's a guide for checking and adjusting extruder steps/mm value. Though thick marker lines are not the best for measurement.

          You can also measure how much filament exits your bowden tube with calipers when you move it from printer LCD.

          If you don't want to mess around with firmware and steps/mm settings, you can adjust flow rate in Cura, although in that case you'll have to experiment with it and waste even more filament. I'd advise you to check for other possible issues first.



          As the other answer has said, this could be caused by temperature creep too, with similar symptoms - filament melting in the heatbreak.



          A long and bendy bowden tube could cause issues, but I'd expect underextrusion+grinding from that, whereas you don't see any underextrusion. Just to be sure, you could try pushing filament by hand (with other hand holding the lever on your extruder to release the filament) - it shouldn't take much force to move it all the way to extruder, and it shouldn't take much force to push it through the hotend either.

          Yet another thing to check is whether your filament gets dented by the extruder gear during normal print. Just insert it until the hotend without holding the lever on extruder and pull it out - it should be as smooth and round as it was before insertion. If it has dents from the extruder gear, that could also be the source of your problems. In that case, you'll need to reduce tension on your extruder spring, or if it's non-adjustable, then get another spring or shorten the existing one.



          As the last thing to check, does this happen with other filaments, especially single-color ones? Maybe this particular filament doesn't play nice with your hotend because of those black dot inclusions.



          So, short list of things to check:



          1. Check extruder steps/mm


          2. Check force on pushing filament through bowden tube (by hand)


          3. Check extruder gear tension


          4. Try another filament







          share|improve this answer












          share|improve this answer



          share|improve this answer










          answered Jan 17 at 12:34









          knahknah

          441




          441











          • $begingroup$
            Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
            $endgroup$
            – DonaldEnte
            Jan 17 at 19:59











          • $begingroup$
            One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
            $endgroup$
            – DonaldEnte
            Jan 17 at 20:13










          • $begingroup$
            @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
            $endgroup$
            – knah
            Jan 18 at 0:22










          • $begingroup$
            @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
            $endgroup$
            – 0scar
            Jan 18 at 10:26










          • $begingroup$
            Why did you add the middle piece of filament, it would never come out a tube like that...
            $endgroup$
            – 0scar
            Jan 18 at 10:30
















          • $begingroup$
            Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
            $endgroup$
            – DonaldEnte
            Jan 17 at 19:59











          • $begingroup$
            One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
            $endgroup$
            – DonaldEnte
            Jan 17 at 20:13










          • $begingroup$
            @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
            $endgroup$
            – knah
            Jan 18 at 0:22










          • $begingroup$
            @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
            $endgroup$
            – 0scar
            Jan 18 at 10:26










          • $begingroup$
            Why did you add the middle piece of filament, it would never come out a tube like that...
            $endgroup$
            – 0scar
            Jan 18 at 10:30















          $begingroup$
          Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
          $endgroup$
          – DonaldEnte
          Jan 17 at 19:59





          $begingroup$
          Thank you very much for your help! I will try to fix these issues. Actually, the end of the filament i pull out is thicker than 1.75mm so that might be it!
          $endgroup$
          – DonaldEnte
          Jan 17 at 19:59













          $begingroup$
          One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
          $endgroup$
          – DonaldEnte
          Jan 17 at 20:13




          $begingroup$
          One more question: i adjusted my extruder gear tension so that it is just right (lower and the filament slips and higher tension and the filament gets extremely dented) but even though i think its good like that, my filament is not perfectly round after pulling it out of the bowden.. Until now i thought, that would be normal. Its not too bad just small knurls of the extruder gear.
          $endgroup$
          – DonaldEnte
          Jan 17 at 20:13












          $begingroup$
          @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
          $endgroup$
          – knah
          Jan 18 at 0:22




          $begingroup$
          @DonaldEnte well, there are tolerances for filament width and smoothness, so if the gear only deforms it a tiny bit, it could be fine. Severely deformed filament could easily get stuck in the hotend though. Compare your knurls to what I have on the right on the photo - what I had probably also caused issues for me. Also could be unusually soft filament.
          $endgroup$
          – knah
          Jan 18 at 0:22












          $begingroup$
          @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
          $endgroup$
          – 0scar
          Jan 18 at 10:26




          $begingroup$
          @DonaldEnte It is very normal the the end is thicker! Nothing to worry about, the filament is 1.75 mm, the liners 2 mm, that explains the thicker end.
          $endgroup$
          – 0scar
          Jan 18 at 10:26












          $begingroup$
          Why did you add the middle piece of filament, it would never come out a tube like that...
          $endgroup$
          – 0scar
          Jan 18 at 10:30




          $begingroup$
          Why did you add the middle piece of filament, it would never come out a tube like that...
          $endgroup$
          – 0scar
          Jan 18 at 10:30











          6












          $begingroup$

          Stringing?



          The stringing is explained by your relatively low retraction settings, 1.5 mm is not much for a Bowden setup. As do too high printing temperatures.



          Stopping mid printing?



          What you are experiencing is called clogging, the extruder cannot push the filament through the hotend and cause the grinding you report. Clogging mid printing is usually caused by insufficient cooling (for the temperature you print at) of the cold end (causing heat creep; slowly increasing temperature of the heat break), especially all-metal hotend assemblies are notoriously known for this problem.



          Your Bowden tube does make a lot of kinks, maybe you can improve the path of the Bowden tube. Also if you are concerned about the sharp filament intake angle, you could print a filament guide:



          Creality CR-10 extruder assembly with filament guide






          share|improve this answer











          $endgroup$












          • $begingroup$
            Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
            $endgroup$
            – DonaldEnte
            Jan 16 at 14:40






          • 3




            $begingroup$
            @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
            $endgroup$
            – Pᴀᴜʟsᴛᴇʀ2
            Jan 16 at 14:45






          • 1




            $begingroup$
            Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
            $endgroup$
            – anaximander
            Jan 16 at 16:06
















          6












          $begingroup$

          Stringing?



          The stringing is explained by your relatively low retraction settings, 1.5 mm is not much for a Bowden setup. As do too high printing temperatures.



          Stopping mid printing?



          What you are experiencing is called clogging, the extruder cannot push the filament through the hotend and cause the grinding you report. Clogging mid printing is usually caused by insufficient cooling (for the temperature you print at) of the cold end (causing heat creep; slowly increasing temperature of the heat break), especially all-metal hotend assemblies are notoriously known for this problem.



          Your Bowden tube does make a lot of kinks, maybe you can improve the path of the Bowden tube. Also if you are concerned about the sharp filament intake angle, you could print a filament guide:



          Creality CR-10 extruder assembly with filament guide






          share|improve this answer











          $endgroup$












          • $begingroup$
            Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
            $endgroup$
            – DonaldEnte
            Jan 16 at 14:40






          • 3




            $begingroup$
            @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
            $endgroup$
            – Pᴀᴜʟsᴛᴇʀ2
            Jan 16 at 14:45






          • 1




            $begingroup$
            Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
            $endgroup$
            – anaximander
            Jan 16 at 16:06














          6












          6








          6





          $begingroup$

          Stringing?



          The stringing is explained by your relatively low retraction settings, 1.5 mm is not much for a Bowden setup. As do too high printing temperatures.



          Stopping mid printing?



          What you are experiencing is called clogging, the extruder cannot push the filament through the hotend and cause the grinding you report. Clogging mid printing is usually caused by insufficient cooling (for the temperature you print at) of the cold end (causing heat creep; slowly increasing temperature of the heat break), especially all-metal hotend assemblies are notoriously known for this problem.



          Your Bowden tube does make a lot of kinks, maybe you can improve the path of the Bowden tube. Also if you are concerned about the sharp filament intake angle, you could print a filament guide:



          Creality CR-10 extruder assembly with filament guide






          share|improve this answer











          $endgroup$



          Stringing?



          The stringing is explained by your relatively low retraction settings, 1.5 mm is not much for a Bowden setup. As do too high printing temperatures.



          Stopping mid printing?



          What you are experiencing is called clogging, the extruder cannot push the filament through the hotend and cause the grinding you report. Clogging mid printing is usually caused by insufficient cooling (for the temperature you print at) of the cold end (causing heat creep; slowly increasing temperature of the heat break), especially all-metal hotend assemblies are notoriously known for this problem.



          Your Bowden tube does make a lot of kinks, maybe you can improve the path of the Bowden tube. Also if you are concerned about the sharp filament intake angle, you could print a filament guide:



          Creality CR-10 extruder assembly with filament guide







          share|improve this answer














          share|improve this answer



          share|improve this answer








          edited Jan 16 at 16:13

























          answered Jan 16 at 14:26









          0scar0scar

          11.1k31546




          11.1k31546











          • $begingroup$
            Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
            $endgroup$
            – DonaldEnte
            Jan 16 at 14:40






          • 3




            $begingroup$
            @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
            $endgroup$
            – Pᴀᴜʟsᴛᴇʀ2
            Jan 16 at 14:45






          • 1




            $begingroup$
            Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
            $endgroup$
            – anaximander
            Jan 16 at 16:06

















          • $begingroup$
            Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
            $endgroup$
            – DonaldEnte
            Jan 16 at 14:40






          • 3




            $begingroup$
            @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
            $endgroup$
            – Pᴀᴜʟsᴛᴇʀ2
            Jan 16 at 14:45






          • 1




            $begingroup$
            Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
            $endgroup$
            – anaximander
            Jan 16 at 16:06
















          $begingroup$
          Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
          $endgroup$
          – DonaldEnte
          Jan 16 at 14:40




          $begingroup$
          Thank you, I will try to fix those things. Do you think my problem is software related or is it the hardware? I can only fix this issue by buying a new hotend?
          $endgroup$
          – DonaldEnte
          Jan 16 at 14:40




          3




          3




          $begingroup$
          @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
          $endgroup$
          – Pᴀᴜʟsᴛᴇʀ2
          Jan 16 at 14:45




          $begingroup$
          @DonaldEnte - Get known issues fixed first, then move onto the next problem (if there is a "next problem*). I'm betting your main issues are mechanical having to do mainly with the Bowden tube and how it is run ... that's some pretty healthy kinking going on there.
          $endgroup$
          – Pᴀᴜʟsᴛᴇʀ2
          Jan 16 at 14:45




          1




          1




          $begingroup$
          Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
          $endgroup$
          – anaximander
          Jan 16 at 16:06





          $begingroup$
          Clogging implies heat creep, and heat creep implies overly hot printing temperature (assuming that the heat break cooling is vaguely normal). Printing too hot can also cause excessive stringing, so reducing print temp might kill two birds with one stone.
          $endgroup$
          – anaximander
          Jan 16 at 16:06












          -1












          $begingroup$

          I had the same thing! On my anycubic I3 mega.



          Tried a lot of stuff and got so sick of it so I installed a 10:1 gearbox on my extruder motor. So now it provides 10x more torque and since I havent got the issue anymore where the extruder is just grinding on the filament and the motor is just skipping steps.



          No because of this and because my anycubic won't connect to a pc I can't change settings on my printer so I resolve the ratio with 1000% flow in my cura settings. And other stuff is also affected.



          But at least it won't stop and just be sitting there and skipping steps.






          share|improve this answer









          $endgroup$








          • 2




            $begingroup$
            This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
            $endgroup$
            – Davo
            Jan 18 at 13:04















          -1












          $begingroup$

          I had the same thing! On my anycubic I3 mega.



          Tried a lot of stuff and got so sick of it so I installed a 10:1 gearbox on my extruder motor. So now it provides 10x more torque and since I havent got the issue anymore where the extruder is just grinding on the filament and the motor is just skipping steps.



          No because of this and because my anycubic won't connect to a pc I can't change settings on my printer so I resolve the ratio with 1000% flow in my cura settings. And other stuff is also affected.



          But at least it won't stop and just be sitting there and skipping steps.






          share|improve this answer









          $endgroup$








          • 2




            $begingroup$
            This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
            $endgroup$
            – Davo
            Jan 18 at 13:04













          -1












          -1








          -1





          $begingroup$

          I had the same thing! On my anycubic I3 mega.



          Tried a lot of stuff and got so sick of it so I installed a 10:1 gearbox on my extruder motor. So now it provides 10x more torque and since I havent got the issue anymore where the extruder is just grinding on the filament and the motor is just skipping steps.



          No because of this and because my anycubic won't connect to a pc I can't change settings on my printer so I resolve the ratio with 1000% flow in my cura settings. And other stuff is also affected.



          But at least it won't stop and just be sitting there and skipping steps.






          share|improve this answer









          $endgroup$



          I had the same thing! On my anycubic I3 mega.



          Tried a lot of stuff and got so sick of it so I installed a 10:1 gearbox on my extruder motor. So now it provides 10x more torque and since I havent got the issue anymore where the extruder is just grinding on the filament and the motor is just skipping steps.



          No because of this and because my anycubic won't connect to a pc I can't change settings on my printer so I resolve the ratio with 1000% flow in my cura settings. And other stuff is also affected.



          But at least it won't stop and just be sitting there and skipping steps.







          share|improve this answer












          share|improve this answer



          share|improve this answer










          answered Jan 18 at 6:56









          MikeMike

          11




          11







          • 2




            $begingroup$
            This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
            $endgroup$
            – Davo
            Jan 18 at 13:04












          • 2




            $begingroup$
            This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
            $endgroup$
            – Davo
            Jan 18 at 13:04







          2




          2




          $begingroup$
          This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
          $endgroup$
          – Davo
          Jan 18 at 13:04




          $begingroup$
          This does not really answer the question. If you have a different question, you can ask it by clicking Ask Question. You can also add a bounty to draw more attention to this question once you have enough reputation. - From Review
          $endgroup$
          – Davo
          Jan 18 at 13:04





          protected by 0scar Jan 18 at 9:04



          Thank you for your interest in this question.
          Because it has attracted low-quality or spam answers that had to be removed, posting an answer now requires 10 reputation on this site (the association bonus does not count).



          Would you like to answer one of these unanswered questions instead?


          Popular posts from this blog

          How to check contact read email or not when send email to Individual?

          Displaying single band from multi-band raster using QGIS

          How many registers does an x86_64 CPU actually have?